National Tsing Hua University Institutional Repository:Vertically-aligned carbon nanotubes prepared by water-assisted chemical vapor deposition
English  |  正體中文  |  简体中文  |  全文筆數/總筆數 : 54367/62174 (87%)
造訪人次 : 15186901      線上人數 : 92
RC Version 6.0 © Powered By DSPACE, MIT. Enhanced by NTHU Library IR team.
搜尋範圍 查詢小技巧:
  • 您可在西文檢索詞彙前後加上"雙引號",以獲取較精準的檢索結果
  • 若欲以作者姓名搜尋,建議至進階搜尋限定作者欄位,可獲得較完整資料
  • 進階搜尋
    National Tsing Hua University Institutional Repository > 工學院  > 材料科學工程學系 > 期刊論文 >  Vertically-aligned carbon nanotubes prepared by water-assisted chemical vapor deposition


    題名: Vertically-aligned carbon nanotubes prepared by water-assisted chemical vapor deposition
    作者: C.-C. Yang;J.-L. Hu;J.-H. Huang
    教師: 黃金花
    日期: 2008
    出版者: Elsevier
    關聯: Diamond and Related Materials,Volume 17,Issue 12,December 2008,Pages 2084-2088
    關鍵詞: Carbon nanotubes
    Water vapor
    Chemical vapor deposition
    摘要: Vertically-aligned single walled carbon nanotubes (V-SWNTs) were prepared by water-assisted and ethylene-pyrolyzing chemical vapor deposition. Water vapor was introduced into the growth environment by passing a small fraction of Ar carrier gas through a water bubbler. The effects of processing gas flow rate, growth time, and water vapor content on the growth of SWNTs using Mo/Fe as the catalyst were systematically studied. For the catalyst of SWNTs growth, multi-metal layers consisting of an Al underlayer with 10 nm in thickness and Mo/Fe layers on top were deposited onto the silica film. Evidences of V-SWNTs with high-purity were found by Raman spectroscopy and TEM morphology. The trace amount of water vapor enhanced the activity of metal catalysts to further assist the growth of SWNTs. For the Mo (0.5 nm)/Fe (1 nm) structure, V-SWNTs grew from surface when the growth time lasted 10 min shown in SEM diagram meanwhile the portion of SWNTs increased until 30 min and then a layer of SWNTs developed shown in the RBM peak in the Raman spectra.