National Tsing Hua University Institutional Repository:A novel process for fabricating electrical contact SnO2/Ag composites by reciprocating extrusion
English  |  正體中文  |  简体中文  |  全文筆數/總筆數 : 54367/62174 (87%)
造訪人次 : 13562350      線上人數 : 62
RC Version 6.0 © Powered By DSPACE, MIT. Enhanced by NTHU Library IR team.
搜尋範圍 查詢小技巧:
  • 您可在西文檢索詞彙前後加上"雙引號",以獲取較精準的檢索結果
  • 若欲以作者姓名搜尋,建議至進階搜尋限定作者欄位,可獲得較完整資料
  • 進階搜尋
    National Tsing Hua University Institutional Repository > 工學院  > 材料科學工程學系 > 期刊論文 >  A novel process for fabricating electrical contact SnO2/Ag composites by reciprocating extrusion


    請使用永久網址來引用或連結此文件: http://nthur.lib.nthu.edu.tw/dspace/handle/987654321/62290


    題名: A novel process for fabricating electrical contact SnO2/Ag composites by reciprocating extrusion
    作者: Chen YL;Yang CF;Yeh JW;Hung SS;Lee SW
    教師: 葉均蔚
    日期: 2005
    出版者: Springer Verlag
    關聯: METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE,Volume: 36A,Issue: 9,Pages: 2441-2447,Published: SEP 2005
    關鍵詞: THERMAL-EXPANSION
    BEHAVIOR
    ALLOYS
    ARC
    摘要: Reciprocating extrusion combined with simple powder compaction was used to produce electrical contact SnO2/Ag composites from Ag and SnO2 powders with improved properties. The SnO2 particles were uniformly dispersed in the Ag matrix after 20 passes of extrusion. The hardness of the composites increased with extrusion passes and leveled off after ten passes, whereas the electrical conductivity decreased slowly after five passes. The variation of the coefficient of thermal expansion with temperature revealed that SnO2/Ag interface strength increased with extrusion passes and was greatest after 20 passes. The SnO2/Ag composites with 20 passes showed the best electrical contact properties in which there was no mass loss through mass transfer from cathode to anode during the make-break erosion test at both low and high current conditions. On the other hand, SnO2/Ag composites with one pass and commercial SnO2-In2O3/Ag specimens had an apparent mass loss under the same condition. Electrical contact composites produced by the present method are promising in electrical contact applications in consideration of cost and performance.
    URI: http://www.springerlink.com/
    http://nthur.lib.nthu.edu.tw/dspace/handle/987654321/62290
    顯示於類別:[材料科學工程學系] 期刊論文

    文件中的檔案:

    檔案 描述 大小格式瀏覽次數
    index.html0KbHTML1229檢視/開啟


    在NTHUR中所有的資料項目都受到原著作權保護,僅提供學術研究及教育使用,敬請尊重著作權人之權益。若須利用於商業或營利,請先取得著作權人授權。
    若發現本網站收錄之內容有侵害著作權人權益之情事,請權利人通知本網站管理者(smluo@lib.nthu.edu.tw),管理者將立即採取移除該內容等補救措施。

    SFX Query

    與系統管理員聯絡

    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - 回饋