National Tsing Hua University Institutional Repository:Growth and characterization of Ga0.65In0.35P orange light-emitting diodes by metalorganic vapor phase epitaxy
English  |  正體中文  |  简体中文  |  全文笔数/总笔数 : 54367/62174 (87%)
造访人次 : 14170657      在线人数 : 54
RC Version 6.0 © Powered By DSPACE, MIT. Enhanced by NTHU Library IR team.
搜寻范围 查询小技巧:
  • 您可在西文检索词汇前后加上"双引号",以获取较精准的检索结果
  • 若欲以作者姓名搜寻,建议至进阶搜寻限定作者字段,可获得较完整数据
  • 进阶搜寻
    National Tsing Hua University Institutional Repository > 電機資訊學院 > 電機工程學系 > 期刊論文 >  Growth and characterization of Ga0.65In0.35P orange light-emitting diodes by metalorganic vapor phase epitaxy


    jsp.display-item.identifier=請使用永久網址來引用或連結此文件: http://nthur.lib.nthu.edu.tw/dspace/handle/987654321/71584


    题名: Growth and characterization of Ga0.65In0.35P orange light-emitting diodes by metalorganic vapor phase epitaxy
    作者: LIN JF;WU MC;JOU MJ;CHANG CM;CHEN CY;LEE BJ
    教師: 吳孟奇
    日期: 1993
    出版者: American Institute of Physics
    關聯: JOURNAL OF APPLIED PHYSICS, American Institute of Physics, Volume 74,   Issue 3, AUG 1 1993, Pages 1781-1786
    关键词: VISIBLE LASER-DIODES
    BAND-GAP ENERGY
    TEMPERATURE OPERATION
    ACTIVE-LAYER
    GA0.5IN0.5P
    DEPOSITION
    IN1-XGAXP
    MOVPE
    LUMINESCENCE
    MECHANISM
    摘要: p-n Ga0.65In0.35P homostructure light-emitting diodes grown on GaAs0.7P0.3 substrates have been fabricated by low-pressure metalorganic vapor-phase epitaxy. The growth and characterization of undoped, Si-, and Zn-doped layers are described in detail. The optimum growth condition to grow the high-quality Ga0.65In0.35P epitaxial layers is at the growth temperatures of 700-740-degrees-C and V/III ratios of 100-200. The strongest photoluminescence peak intensity occurs at 2 x 10(18) and 7 x 10(17) cm-3 for electron and hole concentrations, respectively. Diodes fabricated from the p-n homostructure are characterized by current-voltage measurement, electroluminescence, and external quantum efficiency. A forward-bias turn-on voltage of 1.68 V with an ideality factor of 2.5 and a breakdown voltage of 9 V are obtained from the current-voltage measurements. The emission peak wavelength and full width at half-maximum of electroluminescence are around 610 nm and 79 meV at 20 mA. The external quantum efficiency of the uncoated diode is about 0.015%.
    相関连結: http://www.aip.org/
    URI: http://nthur.lib.nthu.edu.tw/dspace/handle/987654321/71584
    显示于类别:[電機工程學系] 期刊論文

    文件中的档案:

    档案 描述 大小格式浏览次数
    2030154010128.pdf1335KbAdobe PDF395检视/开启


    在NTHUR中所有的資料項目都受到原著作權保護,僅提供學術研究及教育使用,敬請尊重著作權人之權益。若須利用於商業或營利,請先取得著作權人授權。
    若發現本網站收錄之內容有侵害著作權人權益之情事,請權利人通知本網站管理者(smluo@lib.nthu.edu.tw),管理者將立即採取移除該內容等補救措施。

    SFX Query

    與系統管理員聯絡

    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - 回馈