    National Tsing Hua University Institutional Repository > 電機資訊學院 > 電機工程學系 > 期刊論文 >  Very Low Temperature Polycrystalline Silicon Films with Very Large Grains Deposited for Thin Film Transistors Application


    jsp.display-item.identifier=請使用永久網址來引用或連結此文件: http://nthur.lib.nthu.edu.tw/dspace/handle/987654321/72442


    题名: Very Low Temperature Polycrystalline Silicon Films with Very Large Grains Deposited for Thin Film Transistors Application
    作者: K.C. Wang;T.R. Yew;H.L.Hwang
    教師: 黃惠良
    日期: 1996
    出版者: Elsevier
    關聯: Applied Surface Science, Elsevier, Volume 92, Issue 1-4, Feb 2 1996, Pages 99-1054
    关键词: Chemical vapor deposition
    Low temperature operations
    Passivation
    摘要: This paper presents the results of low temperature polycrystalline silicon growth on SiO2 and glass substrates. The silicon films were deposited with the hydrogen dilution method by electron cyclotron resonance chemical vapor deposition at or below 250°C without any thermal annealing. Hydrogen passivation of the SiO2 surface was applied to enhance the grain growth of poly-Si deposition. The polycrystallinity of the silicon films was established by transmission electron microscopy (TEM), Raman scattering, and X-ray diffraction. The maximum grain size was about 1 μm. The crystalline fraction of the polycrystalline silicon (poly-Si) films was near 100% as identified by Raman shift spectra. The preferred orientations of the poly-Si film were 〈110〉 and 〈111〉. Poly-Si films with a maximum grain size of 7000 angstrom were formed at a substrate temperature as low as 100°C
    相関连結: http://www.elsevier.com/
    URI: http://nthur.lib.nthu.edu.tw/dspace/handle/987654321/72442
    显示于类别:[電機工程學系] 期刊論文

    文件中的档案:

    档案 描述 大小格式浏览次数
    index.html0KbHTML401检视/开启


    在NTHUR中所有的資料項目都受到原著作權保護,僅提供學術研究及教育使用,敬請尊重著作權人之權益。若須利用於商業或營利,請先取得著作權人授權。
    若發現本網站收錄之內容有侵害著作權人權益之情事,請權利人通知本網站管理者(smluo@lib.nthu.edu.tw),管理者將立即採取移除該內容等補救措施。

    SFX Query

    與系統管理員聯絡

    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - 回馈